Yttrium-stabilized Zirconia

Yttrium-stabilized zirconia
Yttrium oxide is used as a stabilizer, and this material is mainly tetragonal. It has the highest flexural strength of all zirconia materials, especially when sintered and pressed. Yttrium-stabilized zirconia has a fine grain size, due to its high wear resistance, it is suitable for use in cutting tools for cutting a very sharp corner. The excellent crystal grains make the produced ceramics dense in density, less pores, excellent mechanical strength, corrosion resistance, impact toughness, thermal shock resistance and extremely low thermal conductivity. Due to these characteristics, yttrium-stabilized zirconia is widely used in semiconductor, petrochemical, photovoltaic new energy and other industries.

Yttrium-stabilized zirconia can be used to make crucibles for vacuum induction melting, high-purity zirconium sizing nozzles or zirconium composite long nozzle bricks for steelmaking, etc., and to make furnace linings and gas reaction furnace linings brick with high temperatures above 1800 °C. Because of its semiconductor properties, zirconia products can be made into high temperature electric furnace heating elements, high temperature furnace tubes, wire drawing dies, etc. It can also be made into zirconia components for continuous temperature measurement of high temperature solutions and zirconia components for various oxygen determination instruments. Fused zirconia sand can be used as aggregate for zirconium unshaped materials, foundry sand for titanium alloys and plasma spraying materials. With the development of science and technology, the use of stabilized zirconia is constantly expanding to different fields.

Material properties of Yttrium-stabilized Zirconia ceramic

Description	Unit	Value
Density	G/cm3	5.9~6.05
Water Absorption	%	0
Thermal expansion coefficient	10-6/k	10.5
Young's modulus of elasticity	Gpa	210
Poisson's ratio	/	0.3
Rockwell hardness (HV)	HRA	88~90
Vickers hardness	Gpa	12
Bending strength (room temperature)	MPa	950
Bending Strength (700℃)	MPa	210
Compressive strength (room temperature)	MPa	2000
Fracture toughness	MPa.m1/2	10
Thermal conductivity (room temperature)	W/m.k	2-3
Specific resistivity (room temperature)	Ω.mm2/m	>1015
Operating temperature	℃	1350
Acid and alkali corrosion resistance	/	Strong

The main features of yttrium stabilized zirconia:

• Good mechanical strength
• Excellent wear resistance
• High impact resistance
• Very low conductivity

The main application of yttrium stabilized zirconia:

• Structural Ceramics
• wear parts
• Thermal barrier coating
• Dental ceramics
• Optical fiber
• Ferrules and Bushings
• Grinding media
• Oxygen Sensor